Product Details:
|
Materail: | Isotropic Bonded Neodymium Magnet | Application: | Industrial Magnet,Motor,Automotive,Customized |
---|---|---|---|
Grade: | MGT-NS-230,MGT-NS-240,MGT-NS-250,MGT-NS-260 | Size: | 1mm-100mm ,Customized |
Magetic Direction: | Axial,Radial,Skewed Angel Magnetized,Customized | Environment: | RoHs,Reach,SGS,MSDS |
Coating: | Uncoated,Customized | Color: | Black Or Silver Gray |
High Light: | Isotropic NdFeB Magnets PPS PA12,Bonded NdFeB Magnets PPS PA12,PPS PA12 Injection Molded Magnets |
Isotropic Bonded NdFeB Magnet Injection NdFeB Magnet PA12 SmFeN Magnet
Application
Feature
Anisotropic NdFeB/PA12 Compound for Injection | |||||||
HCNY210L | HCNY212L | HCNY214L | |||||
Unit | |||||||
Magnetic Properties | Residual Induction | Br | mT | 670-730 | 700-750 | 750-820 | |
kGs | 6.7-7.3 | 7.0-7.5 | 7.5-8.2 | ||||
Coercive Force | Hcb | kA/m | 438-478 | 469-501 | 478-517 | ||
kOe | 5.5-6.0 | 5.9-6.3 | 6.0-6.5 | ||||
Intrinsic Coercivity | Hcj | kA/m | 1035-1194 | 1035-1194 | 1035-1194 | ||
kOe | 13.0-15.0 | 13.0-15.0 | 13.0-15.0 | ||||
Max.Product Energy | (BH)max | kJ/cm3 | 75.6-83.6 | 93.9-99.5 | 103.5-111.4 | ||
MGOe | 9.5-10.5 | 11.8-12.5 | 13.0-14.0 | ||||
Physical Properties | Density | ρ | g/cm3 | 4.9-5.2 | 4.9-5.2 | 5.0-5.3 | |
Melt Flowrate | MFR | g/10min | ≥200 | ≥200 | ≥200 | ||
(270℃ 5kg) | |||||||
Shrinkage | % | 0.5-0.7 | 0.5-0.7 | 0.5-0.7 | |||
Tensile Stength | ASTM-D638 | MPa | 48 | 48 | 40 | ||
Flexural Modulus | ASTM-D790 | MPa | 89 | 90 | 80 | ||
Flexural Modulus | ASTM-D790 | Gpa | 15 | 15 | 15 | ||
ZOD Impact Strength | ASTM-D256 | (kJ/m2) | 8.6 | 8.6 | 7 | ||
Injection Molding Process | |||||||
(35ton ) Ring Φ10xΦ7x10 |
Pre drying | ℃/hr | 80/4 | ||||
Barrel Temp. | T1 | ℃ | 250 | 250 | 250 | ||
T2 | ℃ | 270 | 270 | 270 | |||
T3 | ℃ | 275 | 275 | 275 | |||
Mold Temp. | ℃ | 80 | 80 | 80 | |||
Pressure | MPa (kg/cm2) |
70.5 (719) |
70.5 (719) |
70.5 (719) |
|||
Speed | % | 60 | 60 | 60 | |||
1,Molding conditions for customers'reference, the highest temperature of nylon injection barrel is not allowed to exceed 280 degrees. | |||||||
2,It can be customized according to customers'requirements |
Anisotropic NdFeB/PPS Compound for Injection | ||||||
HCNYP80L | HCNYP90L | |||||
Unit | ||||||
Magnetic Properties | Residual Induction | Br | mT | 600-630 | 620-680 | |
kGs | 6.0-6.3 | 6.2-6.8 | ||||
Coercive Force | Hcb | kA/m | 378-418 | 400-438 | ||
kOe | 4.75-5.25 | 5.0-5.5 | ||||
Intrinsic Coercivity | Hcj | kA/m | 1034-1194 | 955-1114 | ||
kOe | 13.0-15.0 | 12.0-14.0 | ||||
Max.Product Energy | (BH)max | kJ/cm3 | 59.7-67.7 | 67.7-75.6 | ||
MGOe | 7.5-8.5 | 8.5-9.5 | ||||
Physical Properties | Density | ρ | g/cm3 | 4.5-4.9 | 4.6-4.9 | |
Melt Flowrate | MFR | g/10min | 300-500 | ≥200 | ||
(330℃ 10kg) | ||||||
Shrinkage | % | 0.05-0.3 | 0.05-0.3 | |||
Tensile Stength | ASTM-D638 | MPa | 56 | 58 | ||
Flexural Modulus | ASTM-D790 | MPa | 98 | 100 | ||
Flexural Modulus | ASTM-D790 | Gpa | 21 | 22 | ||
ZOD Impact Strength | ASTM-D256 | (kJ/m2) | 9.5 | 10 | ||
Injection Molding Process | ||||||
(35ton ) Ring Φ10xΦ7x10 |
Pre drying | ℃/hr | 100/4 | |||
Barrel Temp. | T1 (feed) |
℃ | 290 | 290 | ||
T2 | ℃ | 310 | 310 | |||
T3 (spout) |
℃ | 330 | 330 | |||
Mold Temp. | ℃ | 130 | 130 | |||
Pressure | MPa (kg/cm2) |
70.5 (719) |
70.5 (719) |
|||
Speed | % | 60 | 60 | |||
1, Molding conditions for customers'reference, the highest temperature of nylon injection barrel is not allowed to exceed 350 degrees. | ||||||
2, It can be customized according to customers'requirements |