Product Details:
|
| No: | 20220111-1 | Product Kind: | Compound |
|---|---|---|---|
| Binder: | PA12 | Product Grade: | HCSFY270L |
| L0T.N0: | SFY220111H | Melt Flow Rate （g/10min)270℃ 10kg: | 260 |
| High Light: | ISO9001 Compound SmFeN Magnets,Compound SmFeN Magnets ISO9001,Compound SmFeN HCSFY270L |
||
HCSFY270L Melt Flow Rate (g/10min)270℃ 10kg 260 Compound SmFeN Magnets
SmFeN Magnets
Sm 2 Fe 17 N x rare earth permanent magnet material has excellent endowment magnetic properties, its saturation magnetization strength reaches 1.54T, comparable with Nd-Fe-B's 1.6T; Curie temperature is 470℃ (Nd-Fe-B's 312℃), anisotropic field is 14T (Nd-Fe-B's 8T) are higher than Nd-Fe-B material, its corrosion resistance, thermal stability and Its corrosion resistance, thermal stability and oxidation resistance are all better than Nd-Fe-B material. The thermal stability and oxidation resistance are also better than Nd-Fe-B permanent magnet material, which becomes a new generation of rare earth permanent magnet material. However, the industrialization research on coercivity mechanism, chemical composition optimization, nitriding process and high performance magnet preparation is still incomplete, and a lot of work needs to be done to optimize the magnetic powder processing process and develop new binder and molding methods.
| No. | 20220111-1 | ||||
| Product Kind | Compound | Binder | PA12 | ||
| Product Grade | HCSFY270L | L0T.N0 | SFY220111H | ||
| Delivery Date | 2022-01-11 | Weight(kg) | |||
| Test Item | Required Standard | Test Results | Determine | Remarks | |
| Physical Properties |
Melt Flow Rate (g/10min)270℃ 10kg | 200-300 | 260 | OK | |
| Density(g/cm3) | 4.10-4.40 | 4.27 | OK | ||
| Magnetic Propeties |
Br(kGs) | 5.90-6.30 | 6.14 | OK | |
| Hcb(kOe) | 3.60-4.00 | 4.00 | OK | ||
| Hcj(kOe) | 5.50-6.20 | 5.79 | OK | ||
| (BH)max(MGOe) | 7.00-8.00 | 7.50 | OK | ||
Properties of SmFeN Bagnetic Compound